Paryls® PSU

Paryls ® Polysulfone is a high-strength , high temperature plastic that has practical toughness. It maintains excellent mechanical properties when exposed to steam and offers superior heat resistance to Polycarbonate. It does not offer the impact strength of PPSU.

Key Attributes: Excellent Hydrolytic Stability High Strength Heat Deflection Temperature of 174C. Transparent and Colorable. Capable of 100+ Autoclave Cycles Transparent and Custom Colorable

Typical Applications: Fluid Engineering Medical Devices Membrane Components Animal Containment Food and Beverage Applications

Technical specifications Paryls® PSU

EigenschaftenPropertiesTest-StandardPrüfbedingungen Einheit F3050 NCF3150 NCF3250 NC
StreckspannungTensile strength (yield)ISO 527 -1/-2-MPa757575
Zug-E-ModulTensile modulusISO 527 -1/-2-MPa2.6002.6002.600
BruchdehnungTensile elongation (yield)ISO 527 -1/-2-%5,75,75,7
BruchdehnungTensile elongation (break)ISO 527 -1/-2-%>50>50>50
BiegefestigkeitFlexural strengthISO 178-MPa108108108
BiegemodulFlexural modulusISO 178-MPa2.7002.7002.700
IZOD Kerbschlagzähigkeit gekerbtNotched IZOD ImpactISO 180/A23°CkJ/m25,55,55,5
HDT A (Wärmeformbeständigkeit)HDT/A - Heat Deflection Temp.ISO 75 -1/-21,80 MPa°C175175175
Glasübergangstemperatur, DSCGlass Transition Temp., DSCISO 11357 -1/-210°C/min°C185185185
Spez. DurchgangswiderstandVolume ResistivityIEC 60093100VΩ * m>1E13>1E13>1E13
Spez. OberflächenwiderstandSurface ResistivityIEC 60093100VΩ>1E15>1E15>1E15
DielektrizitätszahlDielectric Constant
IEC 60250
DielektrizitätszahlDielectric Constant
IEC 60250
Dielektrischer VerlustfaktorDissipation factorIEC 60250@100HZE-4888
Dielektrischer VerlustfaktorDissipation factorIEC 60250@1MHZE-4646464
Durchschlagfestigkeit K20/K20Dielectric StrengthIEC 60243-160*60*1mm³KV/mm404040
Vergleichszahl der KriechwegbildungCTIIEC 60112--125125125
DichteDensityISO 118323°Cg/cm³1,241,241,24
WasseraufnahmeWater absorptionISO 6223°C/50% r. F.%0,30,30,3
Schwindung in FließrichtungMold shrinkage (flow)ISO 2577, 294-4--0,60,60,6
Schwindung quer zur FließrichtungMold shrinkage (vertical)ISO 2577, 294-4--0,70,70,7
MFRMelt Flow RateISO 1133343°C/2,16 kgg/10 min5 - 88 - 1313 - 18

General processing information Paryls® PSU

VortrocknungVakuum- oder Trockenlufttrockner 5h bei 160°C6h bei 160°C5h bei 160°C
VerarbeitungstemperaturSpritzguss / Extrusion320° - 370°C320° - 370°C320° - 370°C
WerkzeugtemperaturSpritzguss / Extrusion120 - 160°C120 - 160°C120 - 160°C